Sifat mekanikal
Harta |
Kaedah ujian |
T estingKeadaan |
Suntikan mencetak nilai tipikal |
Percetakan 3D XY Nilai Tipikal |
Nilai Tipikal Pencetakan Z Pencetakan 3D |
Unit |
Kekuatan tegangan |
ISO 527 |
50mm/min |
63.33 |
34.74 ± 4 |
30.34 ± 4 |
MPA |
Pemanjangan pada rehat |
ISO 527 |
50mm/min |
3.31 |
5.18 ± 1 |
1.6 ± 0.2 |
% |
Modulus tegangan |
ISO 527 |
50mm/min |
2408.34 |
2200.4 ± 100 |
2057.5 ± 100 |
MPA |
Kekuatan lentur |
ISO 178 |
2mm/min |
91.04 |
58.36 ± 4 |
44.31 ± 4 |
MPA |
Modulus lentur |
ISO 178 |
2mm/min |
3646.67 |
2326.67 ± 100 |
2057.5 ± 100 |
MPA |
Kekuatan kesan Charpy |
ISO 179 |
23 ℃ |
24.73 |
18 ± 2 |
7.54 ± 1 |
KJ/㎡ |
Kekuatan kesan izod |
ISO 180 |
23 ℃ |
18.1 |
12.66 ± 2 |
6.44 ± 1 |
KJ/㎡ |
Sifat fizikal
Harta |
Kaedah ujian |
Keadaan ujian |
Nilai tipikal |
Unit |
Ketumpatan |
ISO 1183 |
Rendaman |
1.17 |
g/cm3 |
Indeks Aliran Cair (MFR) |
ISO 1133 |
210 ℃/2.16kg |
2-7 |
g/10 min |
Penyerapan kelembapan
Harta |
Kaedah ujian |
Keadaan ujian |
Suntikan mencetak nilai tipikal |
Nilai Tipikal Percetakan 3D |
Unit |
Penyerapan kelembapan |
ISO 62 |
50%RH*23 ℃ |
0.5 |
0.6 |
% |
Sifat kimia
Harta |
Hasil ujian |
Rintangan asid lemah |
Tidak tahan |
Rintangan asid yang kuat |
Tidak tahan |
Rintangan asas yang lemah |
Tidak tahan |
Rintangan asas yang kuat |
Tidak tahan |
Rintangan penyelesaian organik |
Tidak tahan |
Sifat terma
Harta |
Kaedah ujian |
Keadaan ujian |
Suntikan mencetak nilai tipikal |
Percetakan 3D XY Nilai Tipikal |
Nilai Tipikal Pencetakan Z Pencetakan 3D |
Unit |
Suhu peralihan kaca |
DSC |
10 ℃/min |
65.5 |
℃ |
||
Suhu penghabluran |
DSC |
10 ℃/min |
107.7 |
℃ |
||
Titik lebur |
DSC |
10 ℃/min |
147.8 |
℃ |
||
Suhu penyimpangan |
TGA |
20 ℃/min |
N/a |
℃ |
||
Suhu penyimpangan haba |
ISO 75 |
0.45MPa |
57.6 |
55.3 |
56.6 |
℃ |
Suhu penyimpangan haba |
ISO 75 |
1.8mpa |
56.5 |
54.8 |
52.4 |
℃ |
Vicat melembutkan suhu |
ISO 306 |
50 ℃/10n |
61.6 |
59.6 |
60 |
℃ |
Parameter percetakan 3D yang disyorkan
*Berdasarkan muncung 0.4 mm. Keadaan percetakan mungkin berbeza dengan diameter muncung yang berbeza
Suhu percetakan |
210-230 (℃ ℃ |
Suhu katil |
50-60 (℃ ℃) |
Lapisan dinding |
2 lapisan |
Lapisan atas dan bawah |
4 lapisan |
Infill |
100% |
Suhu ambien |
25 ℃ |
Peminat penyejuk |
0-10% |
Kelajuan percetakan |
30 - 50 (mm/s) |
Diameter muncung |
0.4 mm |
Parameter sebenar 3DPrinting
*Semua spesimen mesti ditinggalkan pada suhu bilik selama 24 jam sebelum ujian. Parameter ini didasarkan pada pencetak 3D Bambulab P1S.
Suhu percetakan |
220 ℃ ℃ ℃ |
Suhu katil |
55 (℃ ℃) |
Lapisan dinding |
2 lapisan |
Lapisan atas dan bawah |
4 lapisan |
Infill |
100% |
Suhu ambien |
25 ℃ |
Peminat penyejuk |
10% |
Kelajuan percetakan |
50 (mm/s) |
Diameter muncung |
0.4 mm |
Sifat mekanikal
Harta |
Kaedah ujian |
T estingKeadaan |
Suntikan mencetak nilai tipikal |
Percetakan 3D XY Nilai Tipikal |
Nilai Tipikal Pencetakan Z Pencetakan 3D |
Unit |
Kekuatan tegangan |
ISO 527 |
50mm/min |
63.33 |
34.74 ± 4 |
30.34 ± 4 |
MPA |
Pemanjangan pada rehat |
ISO 527 |
50mm/min |
3.31 |
5.18 ± 1 |
1.6 ± 0.2 |
% |
Modulus tegangan |
ISO 527 |
50mm/min |
2408.34 |
2200.4 ± 100 |
2057.5 ± 100 |
MPA |
Kekuatan lentur |
ISO 178 |
2mm/min |
91.04 |
58.36 ± 4 |
44.31 ± 4 |
MPA |
Modulus lentur |
ISO 178 |
2mm/min |
3646.67 |
2326.67 ± 100 |
2057.5 ± 100 |
MPA |
Kekuatan kesan Charpy |
ISO 179 |
23 ℃ |
24.73 |
18 ± 2 |
7.54 ± 1 |
KJ/㎡ |
Kekuatan kesan izod |
ISO 180 |
23 ℃ |
18.1 |
12.66 ± 2 |
6.44 ± 1 |
KJ/㎡ |
Sifat fizikal
Harta |
Kaedah ujian |
Keadaan ujian |
Nilai tipikal |
Unit |
Ketumpatan |
ISO 1183 |
Rendaman |
1.17 |
g/cm3 |
Indeks Aliran Cair (MFR) |
ISO 1133 |
210 ℃/2.16kg |
2-7 |
g/10 min |
Penyerapan kelembapan
Harta |
Kaedah ujian |
Keadaan ujian |
Suntikan mencetak nilai tipikal |
Nilai Tipikal Percetakan 3D |
Unit |
Penyerapan kelembapan |
ISO 62 |
50%RH*23 ℃ |
0.5 |
0.6 |
% |
Sifat kimia
Harta |
Hasil ujian |
Rintangan asid lemah |
Tidak tahan |
Rintangan asid yang kuat |
Tidak tahan |
Rintangan asas yang lemah |
Tidak tahan |
Rintangan asas yang kuat |
Tidak tahan |
Rintangan penyelesaian organik |
Tidak tahan |
Sifat terma
Harta |
Kaedah ujian |
Keadaan ujian |
Suntikan mencetak nilai tipikal |
Percetakan 3D XY Nilai Tipikal |
Nilai Tipikal Pencetakan Z Pencetakan 3D |
Unit |
Suhu peralihan kaca |
DSC |
10 ℃/min |
65.5 |
℃ |
||
Suhu penghabluran |
DSC |
10 ℃/min |
107.7 |
℃ |
||
Titik lebur |
DSC |
10 ℃/min |
147.8 |
℃ |
||
Suhu penyimpangan |
TGA |
20 ℃/min |
N/a |
℃ |
||
Suhu penyimpangan haba |
ISO 75 |
0.45MPa |
57.6 |
55.3 |
56.6 |
℃ |
Suhu penyimpangan haba |
ISO 75 |
1.8mpa |
56.5 |
54.8 |
52.4 |
℃ |
Vicat melembutkan suhu |
ISO 306 |
50 ℃/10n |
61.6 |
59.6 |
60 |
℃ |
Parameter percetakan 3D yang disyorkan
*Berdasarkan muncung 0.4 mm. Keadaan percetakan mungkin berbeza dengan diameter muncung yang berbeza
Suhu percetakan |
210-230 (℃ ℃ |
Suhu katil |
50-60 (℃ ℃) |
Lapisan dinding |
2 lapisan |
Lapisan atas dan bawah |
4 lapisan |
Infill |
100% |
Suhu ambien |
25 ℃ |
Peminat penyejuk |
0-10% |
Kelajuan percetakan |
30 - 50 (mm/s) |
Diameter muncung |
0.4 mm |
Parameter sebenar 3DPrinting
*Semua spesimen mesti ditinggalkan pada suhu bilik selama 24 jam sebelum ujian. Parameter ini didasarkan pada pencetak 3D Bambulab P1S.
Suhu percetakan |
220 ℃ ℃ ℃ |
Suhu katil |
55 (℃ ℃) |
Lapisan dinding |
2 lapisan |
Lapisan atas dan bawah |
4 lapisan |
Infill |
100% |
Suhu ambien |
25 ℃ |
Peminat penyejuk |
10% |
Kelajuan percetakan |
50 (mm/s) |
Diameter muncung |
0.4 mm |