| Color: | |
|---|---|
| Availability: | |


Mechanica Properties
Property |
Testis Methodo |
T esting Condition |
Typical Precium iniectio CUMATIUM |
3D Typicam Axis Typicam valorem XY |
3D Printing Z Axis Typical Value |
Unitas |
distrahentes Fortitudo |
ISO 527 |
50mm/min |
63.33 |
34.74±4 |
30.34±4 |
MPa |
Elongation at Break |
ISO 527 |
50mm/min |
3.31 |
5.18±1 |
1.6±0.2 |
% |
Modulus distrahens |
ISO 527 |
50mm/min |
2408.34 |
2200.4±100 |
2057.5±100 |
MPa |
Flexurae Fortitudo |
ISO 178 |
2mm/min |
91.04 |
58.36±4 |
44.31±4 |
MPa |
Flexurale Modulus |
ISO 178 |
2mm/min |
3646.67 |
2326.67±100 |
2057.5±100 |
MPa |
Charpy Impact Fortitudo |
ISO 179 |
23℃ |
24.73 |
18±2 |
7.54±1 |
KJ/㎡ |
Izod Impact virtus |
ISO 180 |
23℃ |
18.1 |
12.66±2 |
6.44±1 |
KJ/㎡ |
Corporalia Properties
Property |
Testis Methodo |
Temptans Condition |
Typical Value |
Unitas |
Density |
ISO 1183 |
immersio |
1.17 |
g/cm*3 |
Confluat fluere index (MFR) |
ISO 1133 |
210℃/2.16kg |
2-7 |
g/10 min |
umor Absorption
Property |
Testis Methodo |
Temptans Condition |
Typical Precium iniectio CUMATIUM |
3D Typical Precium Typicam |
Unitas |
umor Absorption |
ISO 62 |
50% RH*23℃ |
0.5 |
0.6 |
% |
Chemical Properties
Property |
Expertus Proventus |
Debilis Acidum Resistentia |
Non obsistens |
Fortis Acidum Repugnantia |
Non obsistens |
Debilis Base Repugnantia |
Non obsistens |
Fortis Base Repugnantia |
Non obsistens |
Solutio organica Resistentia |
Non obsistens |
Scelerisque Properties
Property |
Testis Methodo |
Temptans Condition |
Typical Precium iniectio CUMATIUM |
3D Typicam Axis Typicam valorem XY |
3D Printing Z Axis Typical Value |
Unitas |
Speculum Transitus Temperaturae |
DSC |
10℃/min |
65.5 |
℃ |
||
Crystallization Temperature |
DSC |
10℃/min |
107.7 |
℃ |
||
Liquefactio Point |
DSC |
10℃/min |
147.8 |
℃ |
||
Distortio Temperature |
TGA |
20℃/min |
N/A |
℃ |
||
Calor Distortio Temperature |
ISO 75 |
0.45MPa |
57.6 |
55.3 |
56.6 |
℃ |
Calor Distortio Temperature |
ISO 75 |
1.8MPa |
56.5 |
54.8 |
52.4 |
℃ |
Vicat molliens Temperature |
ISO 306 |
50℃/10N |
61.6 |
59.6 |
60 |
℃ |
Commendatur 3D Press Morbi
*Ex 0.4 mm COLLUM. Condiciones typographicae variari possunt cum diversis diametri COLLUM
Excudendi Temperature |
210-230(℃) |
Lectus Temperature |
50-60(℃) |
Murus Stratis |
2 Stratis |
Summo et imo Stratis |
4 Stratis |
Infill |
100% |
Ambiens Temperature |
25℃ |
Frigus Fan |
0-10% |
Volo excudendi |
30 — 50 mm/s) |
Collum Diameter |
0.4 mm |
3DPrinting Actualis Parametri
*Specimina omnia ad cella temperaturae per 24 horas ante probationem relinquenda sunt. Parametri Bambulab P1S 3D typographi fundantur.
Excudendi Temperature |
220(℃) |
Lectus Temperature |
55(℃) |
Murus Stratis |
2 Stratis |
Summo et imo Stratis |
4 Stratis |
Infill |
100% |
Ambiens Temperature |
25℃ |
Frigus Fan |
10% |
Volo excudendi |
50 mm/s) |
Collum Diameter |
0.4 mm |
Mechanica Properties
Property |
Testis Methodo |
T esting Condition |
Typical Precium iniectio CUMATIUM |
3D Typicam Axis Typicam valorem XY |
3D Printing Z Axis Typical Value |
Unitas |
distrahentes Fortitudo |
ISO 527 |
50mm/min |
63.33 |
34.74±4 |
30.34±4 |
MPa |
Elongation at Break |
ISO 527 |
50mm/min |
3.31 |
5.18±1 |
1.6±0.2 |
% |
Modulus distrahens |
ISO 527 |
50mm/min |
2408.34 |
2200.4±100 |
2057.5±100 |
MPa |
Flexurae Fortitudo |
ISO 178 |
2mm/min |
91.04 |
58.36±4 |
44.31±4 |
MPa |
Flexurale Modulus |
ISO 178 |
2mm/min |
3646.67 |
2326.67±100 |
2057.5±100 |
MPa |
Charpy Impact Fortitudo |
ISO 179 |
23℃ |
24.73 |
18±2 |
7.54±1 |
KJ/㎡ |
Izod Impact virtus |
ISO 180 |
23℃ |
18.1 |
12.66±2 |
6.44±1 |
KJ/㎡ |
Corporalia Properties
Property |
Testis Methodo |
Temptans Condition |
Typical Value |
Unitas |
Density |
ISO 1183 |
immersio |
1.17 |
g/cm*3 |
Confluat fluere index (MFR) |
ISO 1133 |
210℃/2.16kg |
2-7 |
g/10 min |
umor Absorption
Property |
Testis Methodo |
Temptans Condition |
Typical Precium iniectio CUMATIUM |
3D Typical Precium Typicam |
Unitas |
umor Absorption |
ISO 62 |
50% RH*23℃ |
0.5 |
0.6 |
% |
Chemical Properties
Property |
Expertus Proventus |
Debilis Acidum Resistentia |
Non obsistens |
Fortis Acidum Repugnantia |
Non obsistens |
Debilis Base Repugnantia |
Non obsistens |
Fortis Base Repugnantia |
Non obsistens |
Solutio organica Resistentia |
Non obsistens |
Scelerisque Properties
Property |
Testis Methodo |
Temptans Condition |
Typical Precium iniectio CUMATIUM |
3D Typicam Axis Typicam valorem XY |
3D Printing Z Axis Typical Value |
Unitas |
Speculum Transitus Temperaturae |
DSC |
10℃/min |
65.5 |
℃ |
||
Crystallization Temperature |
DSC |
10℃/min |
107.7 |
℃ |
||
Liquefactio Point |
DSC |
10℃/min |
147.8 |
℃ |
||
Distortio Temperature |
TGA |
20℃/min |
N/A |
℃ |
||
Calor Distortion Temperature |
ISO 75 |
0.45MPa |
57.6 |
55.3 |
56.6 |
℃ |
Calor Distortio Temperature |
ISO 75 |
1.8MPa |
56.5 |
54.8 |
52.4 |
℃ |
Vicat molliens Temperature |
ISO 306 |
50℃/10N |
61.6 |
59.6 |
60 |
℃ |
Commendatur 3D Press Morbi
*Ex 0.4 mm COLLUM. Condiciones typographicae variari possunt cum diversis diametri COLLUM
Excudendi Temperature |
210-230(℃) |
Lectus Temperature |
50-60(℃) |
Murus Stratis |
2 Stratis |
Summo et imo Stratis |
4 Stratis |
Infill |
100% |
Ambiens Temperature |
25℃ |
Frigus Fan |
0-10% |
Volo excudendi |
30 — 50 mm/s) |
Collum Diameter |
0.4 mm |
3DPrinting Actualis Parametri
*Specimina omnia ad cella temperaturae per 24 horas ante probationem relinquenda sunt. Parametri Bambulab P1S 3D typographi fundantur.
Excudendi Temperature |
220(℃) |
Lectus Temperature |
55(℃) |
Murus Stratis |
2 Stratis |
Summo et imo Stratis |
4 Stratis |
Infill |
100% |
Ambiens Temperature |
25℃ |
Frigus Fan |
10% |
Volo excudendi |
50 mm/s) |
Collum Diameter |
0.4 mm |