You are here: In domo » Productus » 3D Filamement » Pla » Pla + + 3D printing filamento

Pla + 3D printing filamento

I. Alternatives ad styrene-fundatur materiae
II. Perfectus excudendi superficiebus
III.
Altus rigor IV. Bonum lenta
Bonum
Mechanica
V. Securus ad Colorem VI.
Properties

Diameter: 1.75mm / 2.85mm

Pondus cuiusque volumine: 1KG / 2.5kg

Color:	Ruber Tenebris viride Blue Flavus Pink Alba Hyacinthus METALLICUS Capulus tenebris Cyaneus Cute Niger Griseo Magenta Orange Caeruleus Persici rosea Viride Exercitus Green Brunneis Lux brunneis Tenebris griseo Marmorea Scidero ORCHUS Pomum Viride pinus
Availability:



Inquiro Addere ad cartallum

Comparari cum Traditional PLA, PLA + + FDM 3D printing filamenta habet meliorem fluidos, ita et impulsum resistentia praestat valde bene. PLA + est mutatio, qui est impulsum repugnans, cuius lenta et diuturnitatem est auctus sine afficiens sua praeclarus printing perficientur dum pros de Plaus conservantur. Gratias ad humilitatem warping et princeps accurate, PLA + PLAXS ALUARTUM Superficies quod concedit ut solebat in practical applicationem ubi altius rigorem esse necessitas.

Pla + et PA Share idem environmentally amica formula, sed Pla + habet optimized eius iacuit adhaesionem et integrated vires, tum magis labe.

Aliz-PLA +

Key features

Alternatives ad styrene-fundatur materiae.

Alternatives ad styrene-fundatur materiae.
Perfectus excudendi superficiebus.

Perfectus excudendi superficiebus.
& Loughness Satis

Tough et iacuit adhaesionem PLA + 3D printing filamenta sunt multo altius quam Pla.
Summus

Maximum rigorem boni lenta facile color calor repugnant et praeclara impulsum vires mechanica proprietatibus
Non conteram

Hoc autem non conteram et lenta est auctus vel flexa est crebris. Smooth advenientis materiae durante excudendi ensures stabilis printing et diu opus.
Altior comprehensive proprietas & sumptus perficientur

Est modificatur secundum PLA cum altiorem comprehensive proprietas et pretium perficientur.
Superior lenta impulsum vires

Superior lento impulsum vires, melius æstus stabilitatem et inferioribus involuti rate quam Ordinarius Pla.
Serva omnes pros de Pla

Serva omnes pros de Plaus: upgraded tensile facit non facile conteram; Upgraded eget concedit ut sit pulchellus; Upgraded temperatus ensures qualitas plus mensa; Upgraded materiae adhuc environmental amicitia.

ADVENTIA PLO +

4

DISCIPIO
3
2
1

____________________________

I. Auctus impulsum resistentia: comparari fragilis naturam traditional plasent plasent, PLA + FILAMENT habet optimized formula, quae providet altius lenta, permittens eam ad hauriendum magis industria ante solveret. Est maxime idoneam ad 3D vestigia, quae opus ad sustinere impulsum et accentus.

II. Optimum iacuit adhaesionem: PLA + Filamentum offert fortes interlaer Bonding, significantly improving mechanica vires et structural integritas typis partibus, faciens ultima products magis durabile.

III. Minimal stringing & OOZING: PL PA + FILAMENT habet improved print fluxus perficientur, efficaciter reducing stringing durante excudendi, unde in lautus et levior superficies finiatur et minus post-processus.

IV. Securus ut print: quod retinet user-amica characteres of vexillum Plalament- non calefacit lectum requiritur, humilis caliditas caliditas, faciens idealis pro beginners.

V. Environmentally Sustainable: PLA + FILENT is derived a Renewable Resources (ut Frumentum amulum / Sugarcane) et bonum Biodegradability.

Mechanica proprietatibus

Res	Testis modum	Probatio conditio	Iniectio CUMATIUM Typical valorem	3D printing Xx axis typical pretii	3D excudendi z axem typicam valorem	Unitas
Tensile vires	ISO DXXVII	50mm / min	63.33	34.74 ± IV	30.34 ± IV	MPA
Elongatio ad confractus	ISO DXXVII	50mm / min	3.31	5.18 ± I	1.6 ± 0.2	%
Tensile modulus	ISO DXXVII	50mm / min	2408.34	2200,4 ± C	2057.5 ± C	MPA
Flacalis fortitudinem	ISO CLXXVIII	2mm / min	91.04	58.36 ± IV	44.31 ± IV	MPA
Flexural modulum	ISO CLXXVIII	2mm / min	3646.67	2326,67 ± C	2057.5 ± C	MPA
Charypy Impact fortitudinem	ISO CLXXIX	XXIII ℃	24.73	XVIII ± II	7.54 ± I	KJ / ㎡
Izod impulsum vires	ISO CLXXX	XXIII ℃	18.1	12.66 ± II	6.44 ± I	KJ / ㎡

Physica proprietatibus

Res	Testis modum	Probatio conditio	Typical valorem	Unitas
Densitas	ISO MCLXXXIII	Immersio	1.17	G / CM3
Index fluent (Mfr)	ISO MCXXXIII	CCX ℃ / 2.16kg	2-7	G / X min

Humorem effusio

Res	Testis modum	Probatio conditio	Iniectio CUMATIUM Typical valorem	3D printing typical pretii	Unitas
Humorem effusio	LXII ISO	L% RH * XXIII ℃	0.5	0.6	%

Eget proprietatibus

Res	Probatio effectus
Infirmum acidum resistentia	Non repugnant
Fortis acidum resistentia	Non repugnant
Infirmum basi resistentia	Non repugnant
Fortis basi resistentia	Non repugnant
Organicum solutio resistentia	Non repugnant

Thermal proprietatibus

Res	Testis modum	Probatio conditio	Iniectio CUMATIUM Typical valorem	3D printing Xx axis typical pretii	3D excudendi z axem typicam valorem	Unitas
Vitrum transitus temperatus	DSC	X ℃ / min	65.5			℃
Crystallization temperatus	DSC	X ℃ / min	107.7			℃
Point liquescens	DSC	X ℃ / min	147.8			℃
Distortio temperatus	Tga	XX ℃ / min	N / est			℃
Calor distorsio temperatus	LXXV ISO	0.45MPa	57.6	55.3	56.6	℃
Calor distorsio temperatus	LXXV ISO	1.8MPA	56.5	54.8	52.4	℃
Vicat mollitorum temperatus	ISO CCCVI	L ℃ / 10n	61.6	59.6	60	℃

Commendatur 3D printing parametri

* Ex 0.4 mm CERVIX. Printing conditionibus variantur diversis COLLUM Diametrorum

Typographia temperatus	210-230 (℃)
Tacum temperatus	50-60 (℃)
Muro laminis	II layers
Summo et imo stratis	IV layers
Infleo	C%
Ambientium temperatus	XXV ℃
Refrigerationem fan	0-10%
Celeritas Printing	XXX - L (mm / s)
COLLUM	0,4 mm

3D printing ipsa parametri

* Omnis specimens oportet reliquit ad locus temperatus ad XXIV horas ante tentat. Et parametri sunt secundum Bambulab P1s 3D printer.

Typographia temperatus	CCXX (℃)
Tacum temperatus	LV (℃)
Muro laminis	II layers
Summo et imo stratis	IV layers
Infleo	C%
Ambientium temperatus	XXV ℃
Refrigerationem fan	X%
Celeritas Printing	L (mm / s)
COLLUM	0,4 mm