Airíonna meicniúla
Maoin |
Modh tástála |
T esting riocht |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil 3D Priontáil XY Axis |
Luach tipiciúil priontála 3d z ais z |
Aonad |
Neart teanntachta |
Iso 527 |
50mm/min |
63.33 |
34.74 ± 4 |
30.34 ± 4 |
MPA |
Fadú ag sos |
ISO 527 |
50mm/min |
3.31 |
5.18 ± 1 |
1.6 ± 0.2 |
% |
Modulus teanntachta |
ISO 527 |
50mm/min |
2408.34 |
2200.4 ± 100 |
2057.5 ± 100 |
MPA |
Neart solúbthachta |
ISO 178 |
2mm/min |
91.04 |
58.36 ± 4 |
44.31 ± 4 |
MPA |
Modal Flexural |
ISO 178 |
2mm/min |
3646.67 |
2326.67 ± 100 |
2057.5 ± 100 |
MPA |
Neart tionchair charpy |
ISO 179 |
23 ℃ |
24.73 |
18 ± 2 |
7.54 ± 1 |
Kj/㎡ |
Neart tionchair izod |
ISO 180 |
23 ℃ |
18.1 |
12.66 ± 2 |
6.44 ± 1 |
Kj/㎡ |
Airíonna fisiceacha
Maoin |
Modh tástála |
Riocht tástála |
Luach tipiciúil |
Aonad |
Dlús |
ISO 1183 |
Tuiscintí |
1.17 |
g/cm3 |
Innéacs sreafa leá (MFR) |
ISO 1133 |
210 ℃/2.16kg |
2-7 |
g/10 nóiméad |
Ionsú taise
Maoin |
Modh tástála |
Riocht tástála |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil priontála 3D |
Aonad |
Ionsú taise |
ISO 62 |
50%RH*23 ℃ |
0.5 |
0.6 |
% |
Airíonna ceimiceacha
Maoin |
Toradh tástála |
Friotaíocht aigéad lag |
Ní frithsheasmhach |
Friotaíocht aigéad láidir |
Ní frithsheasmhach |
Friotaíocht bonn lag |
Ní frithsheasmhach |
Friotaíocht bonn láidir |
Ní frithsheasmhach |
Friotaíocht tuaslagáin orgánach |
Ní frithsheasmhach |
Airíonna teirmeacha
Maoin |
Modh tástála |
Riocht tástála |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil 3D Priontáil XY Axis |
Luach tipiciúil priontála 3d z ais z |
Aonad |
Teocht trasdula gloine |
DSc |
10 ℃/min |
65.5 |
℃ |
||
Teocht criostalaithe |
DSc |
10 ℃/min |
107.7 |
℃ |
||
Leáphointe |
DSc |
10 ℃/min |
147.8 |
℃ |
||
Teocht saobhadh |
TGA |
20 ℃/min |
N/A. |
℃ |
||
Teocht saobhadh teasa |
ISO 75 |
0.45MPA |
57.6 |
55.3 |
56.6 |
℃ |
Teocht saobhadh teasa |
ISO 75 |
1.8MPA |
56.5 |
54.8 |
52.4 |
℃ |
Teocht softening vicat |
ISO 306 |
50 ℃/10n |
61.6 |
59.6 |
60 |
℃ |
Paraiméadair priontála 3D molta
*Bunaithe ar 0.4 mm. D'fhéadfadh coinníollacha priontála a bheith éagsúil le trastomhais nozzle éagsúla
Teocht phriontála |
210-230 (℃) |
Teocht na leapa |
50-60 (℃) |
Sraitheanna balla |
2 shraith |
Sraitheanna barr agus bun |
4 Sraitheanna |
Insíotháil |
100% |
Teocht chomhthimpeallach |
25 ℃ |
Lucht leanúna fuaraithe |
0-10% |
Luas priontála |
30 - 50 (mm/s) |
Trastomhas nozzle |
0.4 mm |
Paraiméadair iarbhír 3dprinting
*Ní mór gach eiseamal a fhágáil ag teocht an tseomra ar feadh 24 uair an chloig roimh an tástáil. Tá na paraiméadair bunaithe ar an printéir 3D Bambulab P1S.
Teocht phriontála |
220 (℃) |
Teocht na leapa |
55 (℃) |
Sraitheanna balla |
2 shraith |
Sraitheanna barr agus bun |
4 Sraitheanna |
Insíotháil |
100% |
Teocht chomhthimpeallach |
25 ℃ |
Lucht leanúna fuaraithe |
10% |
Luas priontála |
50 (mm/s) |
Trastomhas nozzle |
0.4 mm |
Airíonna meicniúla
Maoin |
Modh tástála |
T esting riocht |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil 3D Priontáil XY Axis |
Luach tipiciúil priontála 3d z ais z |
Aonad |
Neart teanntachta |
Iso 527 |
50mm/min |
63.33 |
34.74 ± 4 |
30.34 ± 4 |
MPA |
Fadú ag sos |
ISO 527 |
50mm/min |
3.31 |
5.18 ± 1 |
1.6 ± 0.2 |
% |
Modulus teanntachta |
ISO 527 |
50mm/min |
2408.34 |
2200.4 ± 100 |
2057.5 ± 100 |
MPA |
Neart solúbthachta |
ISO 178 |
2mm/min |
91.04 |
58.36 ± 4 |
44.31 ± 4 |
MPA |
Modal Flexural |
ISO 178 |
2mm/min |
3646.67 |
2326.67 ± 100 |
2057.5 ± 100 |
MPA |
Neart tionchair charpy |
ISO 179 |
23 ℃ |
24.73 |
18 ± 2 |
7.54 ± 1 |
Kj/㎡ |
Neart tionchair izod |
ISO 180 |
23 ℃ |
18.1 |
12.66 ± 2 |
6.44 ± 1 |
Kj/㎡ |
Airíonna fisiceacha
Maoin |
Modh tástála |
Riocht tástála |
Luach tipiciúil |
Aonad |
Dlús |
ISO 1183 |
Tuiscintí |
1.17 |
g/cm3 |
Innéacs sreafa leá (MFR) |
ISO 1133 |
210 ℃/2.16kg |
2-7 |
g/10 nóiméad |
Ionsú taise
Maoin |
Modh tástála |
Riocht tástála |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil priontála 3D |
Aonad |
Ionsú taise |
ISO 62 |
50%RH*23 ℃ |
0.5 |
0.6 |
% |
Airíonna ceimiceacha
Maoin |
Toradh tástála |
Friotaíocht aigéad lag |
Ní frithsheasmhach |
Friotaíocht aigéad láidir |
Ní frithsheasmhach |
Friotaíocht bonn lag |
Ní frithsheasmhach |
Friotaíocht bonn láidir |
Ní frithsheasmhach |
Friotaíocht tuaslagáin orgánach |
Ní frithsheasmhach |
Airíonna teirmeacha
Maoin |
Modh tástála |
Riocht tástála |
Múnlú insteallta luach tipiciúil |
Luach tipiciúil 3D Priontáil XY Axis |
Luach tipiciúil priontála 3d z ais z |
Aonad |
Teocht trasdula gloine |
DSc |
10 ℃/min |
65.5 |
℃ |
||
Teocht criostalaithe |
DSc |
10 ℃/min |
107.7 |
℃ |
||
Leáphointe |
DSc |
10 ℃/min |
147.8 |
℃ |
||
Teocht saobhadh |
TGA |
20 ℃/min |
N/A. |
℃ |
||
Teocht saobhadh teasa |
ISO 75 |
0.45MPA |
57.6 |
55.3 |
56.6 |
℃ |
Teocht saobhadh teasa |
ISO 75 |
1.8MPA |
56.5 |
54.8 |
52.4 |
℃ |
Teocht softening vicat |
ISO 306 |
50 ℃/10n |
61.6 |
59.6 |
60 |
℃ |
Paraiméadair priontála 3D molta
*Bunaithe ar 0.4 mm. D'fhéadfadh coinníollacha priontála a bheith éagsúil le trastomhais nozzle éagsúla
Teocht phriontála |
210-230 (℃) |
Teocht na leapa |
50-60 (℃) |
Sraitheanna balla |
2 shraith |
Sraitheanna barr agus bun |
4 Sraitheanna |
Insíotháil |
100% |
Teocht chomhthimpeallach |
25 ℃ |
Lucht leanúna fuaraithe |
0-10% |
Luas priontála |
30 - 50 (mm/s) |
Trastomhas nozzle |
0.4 mm |
Paraiméadair iarbhír 3dprinting
*Ní mór gach eiseamal a fhágáil ag teocht an tseomra ar feadh 24 uair an chloig roimh an tástáil. Tá na paraiméadair bunaithe ar an printéir 3D Bambulab P1S.
Teocht phriontála |
220 (℃) |
Teocht na leapa |
55 (℃) |
Sraitheanna balla |
2 shraith |
Sraitheanna barr agus bun |
4 Sraitheanna |
Insíotháil |
100% |
Teocht chomhthimpeallach |
25 ℃ |
Lucht leanúna fuaraithe |
10% |
Luas priontála |
50 (mm/s) |
Trastomhas nozzle |
0.4 mm |